The Effect of Pressure and Temperature on The Particle Board Manufacture from Palm Oil Empty Bunches and Pine Bark

Asfarizal Saad, Anwar Kasim, Gunawarman Gunawarman, Santosa Santosa


The manufacture of particle boards without synthetic adhesives is influenced by the composition of the material, temperature, time, pressure, particle size and method of manufacture. The pressure of one important parameter and its variations often produce different properties. Pine skin is a waste that is not valuable and just wasted. Making particle boards from palm oil empty bunches and pine bark waste is an interesting and new thing. Pinus merkusii leather powder is used as an added ingredient, its composition is 70% tkks and 30% pine merkusii powder with 5-6% moisture content, dry based. The fiber lengths are 0.1-2.0 cm and pressures are 2, 4, 6, 8 and 10, temperature 150, 160, 170, 180 and 190ºC. The standard for particle board reference and bending test is SNI 03-2105-2006 and ASTM D1037. The result show of working pressure and heating temperature affect the density, moisture content and MOR. Increasing pressure and temperature tend to increase the MOR value and increase in temperature above 190oC, the MOR value decreases.


EFB; pine bark; pressure; temperature; MOR

Full Text:



N. Saari, R. Hashim, O. Sulaiman, and M. Sato, “The Influenced of Compression on Properties of Binderless Compressed Veneer Made from Oil Palm Trunk,” vol. 5, no. 5, pp. 280–283, 2015.

M. K. Sallata, “Pinus Merkusii (Pinus merkusii Jungh et de Vriese) dan Keberadaannya di Kabupaten Tana Toraja, Sulawesi Selatan,” Info Teknis Eboni, vol. 10(2), no. September, pp. 85–98, 2005.

A. Arel, Dira, and A. Setiawati, “Isolasi Senyawa Utama Kulit Batang Tumbuhan Pinus Dari Ekstrak Etil Asetat,” Ilmiah Farmasi, vol. 12, no. 2, pp. 27–35, 2016.

N. Suseno and T. Adiarto, “Ekstraksi Tanin Dari Kulit Kayu Pinus Sebagai Bahan Perekat Briket,” 2014.

F. Kasim and A. Kasim, “Hydrolysis of Oil Palm Empty Fruit Bunch Fibers to Produce Sugar Hydrolyzate as Raw Material for Bioethanol Production,” International Journal on Advanced Science, …, vol. 3, no. 3, pp. 24–27, 2013.

Asfarizal, “The characteristics of Coconut Fiber-Based Composites and Sugar Fiber-Based Composites,” Jurnal Teknik Mesin, vol. 6, no. 1, pp. 24–33, 2016.

Supraptiningsih, “Effect of Banana Stems Fiber Powder as Filler to the Mechanical Properties of PVC-CaCO3 Composite,” Majalah Kulit, vol. 3, pp. 79–87, 2012.

A. Kasim and A. Fuadi, “Influence of Temperature and Pressing Time on Particleboard Processing from Palm Oil Trunk (Elaeis guineensis Jacq.) and Gambir (Uncaria gambir Roxb.) Adhesive on Particleboard Properties,” Wood Science and Technology, pp. 17–21, 2007.

N. Saadaoui, A. Rouilly, K. Fares, and L. Rigal, “Characterization of date palm lignocellulosic by-products and self-bonded composite materials obtained thereof,” Materials and Design, vol. 50, pp. 302–308, 2013.

T. Wu, X. Wang, and K. Kito, “Effects of pressures on the mechanical properties of corn straw bio-board,” Engineering in Agriculture, Environment and Food, vol. 8, no. 3, pp. 123–129, 2015.

R. Hashim et al., “Influence of press temperature on the properties of binderless particleboard made from oil palm trunk,” Materials and Design, vol. 32, no. 1, pp. 2520–2525, 2011.

Indonesian National Standard Agency, “Indonesian National Standard (SNI) for Particle Boards,” BSN, vol. SNI 03-210, p. 15, 2006.

D. Wahyuni and B. P. Lapanporo, “Analisis Sifat Fisik dan Mekanik Papan Partikel Berbahan Dasar Sekam Padi,” Positron, vol. IV, no. 2, pp. 60–63, 2014.

M. C. N. Yemele, A. Koubaa, A. Cloutier, P. Soulounganga, and M. Wolcott, “Effect of bark fiber content and size on the mechanical properties of bark/HDPE composites,” Composites Part A: Applied Science and Manufacturing, vol. 41, no. 1, pp. 131–137, 2010.

J. F. Hunt, W. Leng, and M. Tajvidi, “Vertical density profile and internal bond strength of wet-formed particleboard bonded with cellulose nanofibrils,” Wood and Fiber Science, 2017 49(4): 1-11, vol. 49, no. 4, pp. 1–11, 2017.


  • There are currently no refbacks.

Copyright of JTM (p-ISSN: 2089-4880   e-ISSN:2598-8263)