Analysis of Current, Filler Metal, and Groove on Tensile Strength and Hardness of Dissimilar Welding Using Gas Tungsten Arc Welding (GTAW)
Dissimilar welding commonly used on many industries, for example power plan field. This paper presents the investigations carried out to study the influence of current, filler metal, and groove on 304 Stainless Steel to AISI 1040 Carbon Steel dissimilar joints. Gas Tungsten Arch Welding (GTAW) was conducted to join the both of base metals. 100 and 120 Ampere of current were conducted on this research, V and double-V groove with 70o of the angle as well. The maximum hardness was obtained 623.2 HVN of ER 70S-6 filler metal with 120 A of current and V groove. While the maximum tensile strength was obtained from the joint using ER 308L with 100 A of current and V-groove of 673.74 MPa. The HAZ region was obtained from the joint using double-V groove was wider than HAZ region of joint using V-groove according the macrostructure image of the joints.
X. Yuan, L. Chen, Y. Zhao, H. Di, and F. Zhu, "Influence of annealing temperature on mechanical properties and microstructures of a high manganese austenitic steel," Journal of Materials Processing Technology, vol. 217, pp. 278-285, 2015.
J. A. James and R. Sudhish, "Study on Effect of Interlayer in Friction Welding for Dissimilar Steels: SS 304 and AISI 1040," Procedia Technology, vol. 25, pp. 1191-1198, 2016.
D. Luder, T. Hundhausen, E. Kaminsky, Y. Shor, N. Iddan, S. Ariely, et al., "Failure analysis and metallurgical transitions in SS 304L air pipe caused by local overheating," Engineering Failure Analysis, vol. 59, pp. 292-303, 2016.
X. Y. Wang and D. Y. Li, "Mechanical, electrochemical and tribological properties of nano-crystalline surface of 304 stainless steel," Wear, vol. 255, pp. 836-845, 2003/08/01/ 2003.
A. Setiawan and Y. A. Y. Wardana, "Analisa Ketangguhan dan Struktur Mikro pada Daerah Las dan HAZ Hasil Pengelasan Sumerged Arc Welding pada Baja SM 490," Jurnal Teknik Mesin, vol. 8, pp. pp. 57-63, 2006.
N. Arivazhagan, S. Singh, S. Prakash, and G. M. Reddy, "Investigation on AISI 304 austenitic stainless steel to AISI 4140 low alloy steel dissimilar joints by gas tungsten arc, electron beam and friction welding," Materials & Design, vol. 32, pp. 3036-3050, 2011.
H. Ma, G. Qin, P. Geng, F. Li, B. Fu, and X. Meng, "Microstructure characterization and properties of carbon steel to stainless steel dissimilar metal joint made by friction welding," Materials & Design, vol. 86, pp. 587-597, 2015.
- There are currently no refbacks.
JTM Indexed by:
Copyright of JTM (p-ISSN: 2089-4880 e-ISSN:2598-8263)